Critical behaviour of magnetic losses

摘要: The critical exponent γ of the complex susceptibility χ = χ′ – iχ″ was measured in temperature range 5 × 10−5 ≦ ϵ |T Tc|Tc 10−2 at frequencies between 0.1 and 20 kHz a field mOe for very pure polycrystalline nickel. For real part zero frequency χ′(0) χo(0)ϵ–γ T > Tc 1.41 ± 0.02 is obtained χ′o(0) (3.4 0.8) good agreement with recent theoretical results. Comparison two samples difference purity by factor 10 shows expected “rounding” above Tc. contributions eddy currents, hysteresis, paraprocess, after-effect to were determined separately. loss angle as well Rayleigh contant viscosity constant Sv obey simple power laws below Low losses mean Curie Tc, together behaviour χ(T) indicate presence small ferromagnetic clusters region. Der kritische Exponent de komplexen Suszeptibilitat wurde im Temperaturbereich bei Frequenzen zwischen 0,1 und einem Feld von an sehr reinem polykritallinem Nickel gemessen. Fur χ′o(0)ϵ–γ, erhielten wir 1,41 0,02, sowie (3,4 0,8) 10−5, guter Ubereinstimmung mit neueren theoretischen Ergebnissen. Beim Vergleich zweier Proben einer um den Faktor verschiedenen Reinheit zeigte sich der erwartete Unterschied „Abrundung” oberhalb Der Einflus des Paraprozesses Wirbelstrom-, Hysterese- Nachwirkungs-Verlusten auf die komplexe untersucht. statische Verlustwinkel, Rayleigh-Konstante Nachwirkungskonstante gehorchen einfachen Potenzgesetzen. Die niederfrequenten Verluste mittleren Curietemperatur das Verhalten unterhalb deuten Existenz kleinen ferromagnetisch geordneten Bereichen kritischen Temperaturgebiet hin.