Early Stages of the Wear Behavior of AISI 440C Stainless Steel under Rolling Contact in Water
作者： Takashi Honda , Katsuyuki Kida , Edson Costa Santos , Takuya Shibukawa
DOI: 10.4028/WWW.SCIENTIFIC.NET/AMR.566.654
关键词: Surface roughness 、 Adhesion force 、 Metallurgy 、 Rolling contact fatigue 、 Adhesion 、 Wear loss 、 Composite material 、 Materials science 、 High load 、 Surface conditions
摘要: In the present work, rolling contact fatigue (RCF) tests in water were performed on AISI 440C stainless steels under different loading. Each test was interrupted at 3.6×104, 7.2×104, 1.44×105, 2.16×105, 2.88×105 and rotating cycles wear track stages observed by using a 3D laser confocal microscope. The loss 2100 N significantly higher compared to 500 or 1000 N. surface roughness samples tested increased during severe adhesion entire surface. case of tests, remained low with mild occurring. It is concluded that force levels are high load contact. They greatly influence conditions cause loss.
sci-hub.se 参考文章(7)
F.M. Kustas, M.S. Misra, D.F. Shepard, J.F. Froechtenigt, Tribological performance of hard carbon coatings on 440C bearing steel Surface and Coatings Technology. ,vol. 48, pp. 113- 119 ,(1991) , 10.1016/0257-8972(91)90134-I
C.C Chang, S.K Yen, Characterization of electrolytic ZrO2/Al2O3 double layer coatings on AISI 440C stainless steel Surface & Coatings Technology. ,vol. 182, pp. 242- 250 ,(2004) , 10.1016/S0257-8972(03)00862-4
A.J. Slifka, T.J. Morgan, R. Compos, D.K. Chaudhuri, Wear mechanism maps of 440C martensitic stainless steel Wear. pp. 614- 618 ,(1993) , 10.1016/0043-1648(93)90551-V
H. V. Squires, S. J. Radcliffe, A comparison of the performance of AISI 52100 and AISI 440C ball bearings in a corrosive environment Journal of Materials Science. ,vol. 18, pp. 3611- 3620 ,(1983) , 10.1007/BF00540734
Dilip K. Chaudhuri, Andrew J. Slifka, James D. Siegwarth, Friction and oxidative wear of 440C ball bearing steels under high load and extreme bulk temperatures Wear. ,vol. 160, pp. 37- 50 ,(1993) , 10.1016/0043-1648(93)90404-A
H.K.D.H. Bhadeshia, Steels for bearings Progress in Materials Science. ,vol. 57, pp. 268- 435 ,(2012) , 10.1016/J.PMATSCI.2011.06.002
Ueber die Berührung fester elastischer Körper. Crelle's Journal. ,vol. 1882, pp. 156- 171 ,(1882) , 10.1515/CRLL.1882.92.156