An investigation of fretting fatigue in a circular arc dovetail assembly
作者： Liang Shi , Da-sheng Wei , Yan-rong Wang , Ai-mei Tian , Di Li
DOI: 10.1016/J.IJFATIGUE.2015.07.025
关键词: Composite material 、 Finite element method 、 Dovetail joint 、 Arc (geometry) 、 Range (aeronautics) 、 Materials science 、 Plane (geometry) 、 Stress gradient 、 Structural engineering 、 Fretting 、 Fixture
摘要: … in such a simplified fixture, since it has … fixtures in our study will help reduce the additional bending moment, it is not sufficient to eliminate all misalignment of the upper and lower fixtures…
sci-hub.se 参考文章(38)
DR Swalla, RW Neu, Characterization of Fretting Fatigue Process Volume Using Finite Element Analysis ASTM International. ,(2003) , 10.1520/STP10753S
JA Araújo, D Nowell, Analysis of pad size effects in fretting fatigue using short crack arrest methodologies International Journal of Fatigue. ,vol. 21, pp. 947- 956 ,(1999) , 10.1016/S0142-1123(99)00077-8
Norman E Dowling, Mechanical Behavior of Materials ,(2009)
Da-Sheng Wei, Yan-Rong Wang, Xiao-Guang Yang, Analysis of failure behaviors of dovetail assemblies due to high gradient stress under contact loading Engineering Failure Analysis. ,vol. 18, pp. 314- 324 ,(2011) , 10.1016/J.ENGFAILANAL.2010.09.011
A.E. Giannakopoulos, T.C. Lindley, S. Suresh, Aspects of equivalence between contact mechanics and fracture mechanics: theoretical connections and a life-prediction methodology for fretting-fatigue Acta Materialia. ,vol. 46, pp. 2955- 2968 ,(1998) , 10.1016/S1359-6454(98)00011-1
Da-Sheng Wei, Shan-Hu Yuan, Yan-Rong Wang, Failure analysis of dovetail assemblies under fretting load Engineering Failure Analysis. ,vol. 26, pp. 381- 396 ,(2012) , 10.1016/J.ENGFAILANAL.2012.06.007
Matthew P. Szolwinski, Thomas N. Farris, Mechanics of fretting fatigue crack formation Wear. ,vol. 198, pp. 93- 107 ,(1996) , 10.1016/0043-1648(96)06937-2
Ioannis V. Papadopoulos, Vassilis P. Panoskaltsis, Invariant formulation of a gradient dependent multiaxial high-cycle fatigue criterion Engineering Fracture Mechanics. ,vol. 55, pp. 513- 528 ,(1996) , 10.1016/S0013-7944(96)00047-1
S. Naboulsi, S. Mall, Fretting fatigue crack initiation behavior using process volume approach and finite element analysis Tribology International. ,vol. 36, pp. 121- 131 ,(2003) , 10.1016/S0301-679X(02)00139-1
D. Nowell, D. Dini, Stress gradient effects in fretting fatigue Tribology International. ,vol. 36, pp. 71- 78 ,(2003) , 10.1016/S0301-679X(02)00134-2