The effect of stacking sequence on the bearing strengths of quasi-isotropic composite laminates
作者： P.A. Smith , K.J. Pascoe
DOI: 10.1016/0263-8223(86)90065-6
关键词:
摘要: Abstract The pin-bearing strengths of eight different stacking sequences quasiisotropic CFRP laminates were measured. failure mechanisms studied from scanning electron microscopy the inside hole. An attempt was made to correlate results with a simple estimate interlaminar normal stress distribution around loaded half damage development in presence lateral restraint (from torque-tightened bolt) also examined. In general clamp-up inhibited local bearing (delamination) failure.
elsevier.com
sci-hub.se 参考文章(20)
L. J. Hart-Smith, Mechanically-Fastened Joints for Advanced Composites — Phenomenological Considerations and Simple Analyses Fibrous Composites in Structural Design. pp. 543- 574 ,(1980) , 10.1007/978-1-4684-1033-4_32
M.G. Bader, L. Boniface, The Assessment of Fatigue Damage in CFRP Laminates TEQC83#R##N#Procedings of the International Conference on Testing, Evaluation and Quality Control of Composites. pp. 66- 75 ,(1983) , 10.1016/B978-0-408-22162-7.50011-7
JH Crews, RVA Naik, Failure analysis of a graphite/epoxy laminate subjected to bolt-bearing loads ASTM special technical publications. pp. 115- 133 ,(1986) , 10.1520/STP19983S
N.J. Pagano, R.Byron Pipes, Some observations on the interlaminar strength of composite laminates International Journal of Mechanical Sciences. ,vol. 15, pp. 679- 688 ,(1973) , 10.1016/0020-7403(73)90099-4
Nicholas J. Salamon, An Assessment of the Interlaminar Stress Problem in Laminated Composites Journal of Composite Materials. ,vol. 14, pp. 177- 194 ,(1980) , 10.1177/002199838001400114
W.J. Quinn, F.L. Matthews, The Effect of Stacking Sequence on the Pin-Bearing Strength in Glass Fibre Reinforced Plastic: Journal of Composite Materials. ,vol. 11, pp. 139- 145 ,(1977) , 10.1177/002199837701100202
W.M. Lucking, S.V. Hoa, T.S. Sankar, The Effect of Geometry on Interlaminar Stresses of [0/90]s Composite Laminates with Circular Holes Journal of Composite Materials. ,vol. 18, pp. 188- 198 ,(1984) , 10.1177/002199838401800207
T.A. Collings, On the bearing strengths of cfrp laminates Composites. ,vol. 13, pp. 241- 252 ,(1982) , 10.1016/0010-4361(82)90006-4
Leif Carlsson, Interlaminar Stresses at a Hole in a Composite Member Subjected to In-Plane Loading Journal of Composite Materials. ,vol. 17, pp. 238- 249 ,(1983) , 10.1177/002199838301700305
T.A. Collings, M.J. Beauchamp, Bearing deflection behaviour of a loaded hole in CFRP Composites. ,vol. 15, pp. 33- 38 ,(1984) , 10.1016/0010-4361(84)90958-3