The mechanical behavior of GLARE laminates for aircraft structures
作者： Guocai Wu , J. -M. Yang
DOI: 10.1007/S11837-005-0067-4
关键词:
摘要: … density of GLARE laminate is at least 8% lower than aluminum alloy. GLARE … bond strength between the fiber layers and metal layers. Several GLARE variants with different laminate lay…
springer.com
harvard.edu
sci-hub.se 参考文章(46)
H. J. M. Woerden, J. Sinke, P. A. Hooijmeijer, Maintenance of Glare Structures and Glare as Riveted or Bonded Repair Material Applied Composite Materials. ,vol. 10, pp. 307- 329 ,(2003) , 10.1023/A:1025593314780
R. C. Alderliesten, M. Hagenbeek, J. J. Homan, P. A. Hooijmeijer, T. J. de Vries, C. A. J. R. Vermeeren, Fatigue and damage tolerance of GLARE Applied Composite Materials. ,vol. 10, pp. 223- 242 ,(2003) , 10.1023/A:1025537818644
C. A. J. R. Vermeeren, An Historic Overview of the Development of Fibre Metal Laminates Applied Composite Materials. ,vol. 10, pp. 189- 205 ,(2003) , 10.1023/A:1025533701806
M. Hagenbeek, C. van Hengel, O. J. Bosker, C. A. J. R. Vermeeren, Static Properties of Fibre Metal Laminates Applied Composite Materials. ,vol. 10, pp. 207- 222 ,(2003) , 10.1023/A:1025569316827
Ya-Jun Guo, Xue-Ren Wu, A phenomenological model for predicting crack growth in fiber-reinforced metal laminates under constant-amplitude loading Composites Science and Technology. ,vol. 59, pp. 1825- 1831 ,(1999) , 10.1016/S0266-3538(99)00042-1
A. Vlot, Impact loading on fibre metal laminates International Journal of Impact Engineering. ,vol. 18, pp. 291- 307 ,(1996) , 10.1016/0734-743X(96)89050-6
Dennis A Burianek, S.Mark Spearing, Delamination growth from face sheet seams in cross-ply titanium/graphite hybrid laminates Composites Science and Technology. ,vol. 61, pp. 261- 269 ,(2001) , 10.1016/S0266-3538(00)00206-2
M Kawai, Two-stress level fatigue of unidirectional fiber–metal hybrid composite: GLARE 2 International Journal of Fatigue. ,vol. 24, pp. 567- 580 ,(2002) , 10.1016/S0142-1123(01)00108-6
Ya-Jun Guo, Xue-Ren Wu, Bridging stress distribution in center-cracked fiber reinforced metal laminates: modeling and experiment Engineering Fracture Mechanics. ,vol. 63, pp. 147- 163 ,(1999) , 10.1016/S0013-7944(99)00018-1
J. Macheret, R.J. Bucci, A crack growth resistance curve approach to fiber/metal laminate fracture toughness evaluation Engineering Fracture Mechanics. ,vol. 45, pp. 729- 739 ,(1993) , 10.1016/0013-7944(93)90061-V