Electro-discharge machining (EDM) versus hard turning and grinding—Comparison of residual stresses and surface integrity generated in AISI O1 tool steel
作者： V. García Navas , I. Ferreres , J.A. Marañón , C. Garcia-Rosales , J. Gil Sevillano
DOI: 10.1016/J.JMATPROTEC.2007.04.131
关键词:
摘要: … surface and well below it, accompanied by the formation of a superficial “white layer” where … the service life of the machined parts, because it promotes crack formation and propagation. …
elsevier.com
sci-hub.se 参考文章(26)
Jian Lu, Handbook of Measurement of Residual Stresses ,(1995)
I. C. Noyan, J. B. Cohen, Residual Stress: Measurement by Diffraction and Interpretation ,(1987)
M. G. Moore, W. P. Evans, Mathematical Correction for Stress in Removed Layers in X-Ray Diffraction Residual Stress Analysis SAE Technical Paper Series. ,(1958) , 10.4271/580035
Eugene V Shikin, Alexander I Plis, None, Handbook on Splines for the User ,(1995)
J. Rech, A. Moisan, Surface integrity in finish hard turning of case-hardened steels International Journal of Machine Tools and Manufacture. ,vol. 43, pp. 543- 550 ,(2003) , 10.1016/S0890-6955(02)00141-4
G Cusanelli, A Hessler-Wyser, F Bobard, R Demellayer, R Perez, R Flükiger, Microstructure at submicron scale of the white layer produced by EDM technique Journal of Materials Processing Technology. ,vol. 149, pp. 289- 295 ,(2004) , 10.1016/J.JMATPROTEC.2003.11.047
Bernard Dennis Cullity, Elements of X-ray diffraction ,(1956)
J Barry, G Byrne, TEM study on the surface white layer in two turned hardened steels Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 325, pp. 356- 364 ,(2002) , 10.1016/S0921-5093(01)01447-2
A. Peiter, H. Wern, Simultaneous X‐ray measurements in‐situ of tri‐axial stresses, Poisson's ratio and the stress free lattice spacing Strain. ,vol. 23, pp. 103- 107 ,(1987) , 10.1111/J.1475-1305.1987.TB00628.X
L. C. Lim, L. C. Lee, Y. S. Wong, H. H. Lu, Solidification microstructure of electrodischarge machined surfaces of tool steels Materials Science and Technology. ,vol. 7, pp. 239- 248 ,(1991) , 10.1179/MST.1991.7.3.239