Ductile–brittle transition in micropillar compression of GaAs at room temperature
作者： Fredrik Östlund , Philip R. Howie , Rudy Ghisleni , Sandra Korte , Klaus Leifer
DOI: 10.1080/14786435.2010.509286
关键词:
摘要: Experiments have been carried out on how compressive failure of< 100> axis GaAs micropillars at room temperature is influenced by their diameter. Slip was observed in all micropillars, often on intersecting slip planes. Cracks could nucleate at these intersections and then grow axially in the sample, with bursts of crack growth. However, GaAs micropillars with diameters less than approximately 1 µm did not split, nor was splitting observed where slip occurred on only one plane. The conditions under which such splitting can occur have …
philpapers.org
sci-hub.se 参考文章(29)
F. C. LEA, Hardness of metals C. Griffin. ,(1936)
J. H. Westbrook, Hans Conrad, The Science of hardness testing and its research applications : based on papers presented at a symposium of the American Society for Metals, October 18 to 20, 1971 American Society for Metals. ,(1973)
D. Kiener, C. Motz, M. Rester, M. Jenko, G. Dehm, FIB damage of Cu and possible consequences for miniaturized mechanical tests Materials Science and Engineering A-structural Materials Properties Microstructure and Processing. ,vol. 459, pp. 262- 272 ,(2007) , 10.1016/J.MSEA.2007.01.046
Quasi-static crack propagation Proceedings of The Royal Society A: Mathematical, Physical and Engineering Sciences. ,vol. 299, pp. 508- 524 ,(1967) , 10.1098/RSPA.1967.0152
M. F. Ashby, C. G. Sammis, The damage mechanics of brittle solids in compression Pure and Applied Geophysics. ,vol. 133, pp. 489- 521 ,(1990) , 10.1007/BF00878002
S. J. Lloyd, J. M. Molina-aldareguia, W. J. Clegg, Deformation under nanoindents in sapphire, spinel and magnesia examined using transmission electron microscopy Philosophical Magazine. ,vol. 82, pp. 1963- 1969 ,(2002) , 10.1080/01418610208235708
A. A. Griffith, The Phenomena of Rupture and Flow in Solids Philosophical Transactions of the Royal Society A. ,vol. 221, pp. 163- 198 ,(1921) , 10.1098/RSTA.1921.0006
A.H. Cottrell, LX. The formation of immobile dislocations during slip Philosophical Magazine Series 1. ,vol. 43, pp. 645- 647 ,(1952) , 10.1080/14786440608520220
R. Rabe, J.-M. Breguet, P. Schwaller, S. Stauss, F.-J. Haug, J. Patscheider, J. Michler, Observation of fracture and plastic deformation during indentation and scratching inside the scanning electron microscope Thin Solid Films. ,vol. 469, pp. 206- 213 ,(2004) , 10.1016/J.TSF.2004.08.096
Y. Androussi, G. Vanderschaeve, A. Lefebvre, Slip and twinning in high-stress-deformed GaAs and the influence of doping Philosophical Magazine. ,vol. 59, pp. 1189- 1204 ,(1989) , 10.1080/01418618908221170