Wear of Tin Coating and Al-Si Alloy Substrate Against Carburized Steel Under Mixed Lubrication
作者： Q. Wang , H. S. Cheng , M. E. Fine
DOI: 10.1080/10402009408983293
关键词:
摘要: Tin coatings on Al-Si alloys are widely used in the automotive industries. The soft tin coating and harder substrate alloy form a tribological system with advantages of low friction reasonably high load-bearing capacity. Wear tests coated Z332 conformal contact against carburized 1016 steel have been carried out under mixed lubrication SAE WW30 oil to study wear, mechanisms. Two major wear mechanisms, uniform due micro-plowing spall pitting related found contribute bearing material loss when fluid film is relatively thick (A about 1.6). Under conditions thinner films ˜ 0.8), some local debonding occurs. closely fracture substrate. bonding between silicon seems be weaker than aluminum tin. During oxidation Presented as Society Tribologists Lubrication Engineers pa...
harvard.edu
sci-hub.se 参考文章(8)
C. J. Thwaites, B. T. K. Barry, Tin and its alloys and compounds Ellis Horwood , Halsted Press. ,(1983)
P. K. Goenka, Analytical Curve Fits for Solution Parameters of Dynamically Loaded Journal Bearings Journal of Tribology-transactions of The Asme. ,vol. 106, pp. 421- 427 ,(1984) , 10.1115/1.3260950
G.A. Hoskin, J.W. Provan, J.E. Gruzleski, The in-situ fatigue testing of a cast aluminum-silicon alloy Theoretical and Applied Fracture Mechanics. ,vol. 10, pp. 27- 41 ,(1988) , 10.1016/0167-8442(88)90054-7
B.N.Pramila Bai, E.S. Dwarakadasa, S.K. Biswas, Subsurface damage in dry wear of Al-Si alloys Wear. ,vol. 71, pp. 381- 384 ,(1981) , 10.1016/0043-1648(81)90234-9
K.Mohammed Jasim, E.S. Dwarakadasa, Wear in Al-Si alloys under dry sliding conditions Wear. ,vol. 119, pp. 119- 130 ,(1987) , 10.1016/0043-1648(87)90102-5
B. N. Pramila Bai, S. K. Biswas, Effect of Load on Dry Sliding Wear of Aluminum-Silicon Alloys Tribology Transactions. ,vol. 29, pp. 116- 120 ,(1986) , 10.1080/05698198608981667
J. F. Booker, Dynamically Loaded Journal Bearings: Mobility Method of Solution Journal of Basic Engineering. ,vol. 87, pp. 537- 546 ,(1965) , 10.1115/1.3650602
J. A. Greenwood, J. H. Tripp, The Contact of Two Nominally Flat Rough Surfaces Proceedings of the Institution of Mechanical Engineers. ,vol. 185, pp. 625- 633 ,(1970) , 10.1243/PIME_PROC_1970_185_069_02