Identification and validation of an enhanced mesomodel for laminated composites within the WWFE-III
作者： Federica Daghia , Pierre Ladeveze
关键词:
摘要: The accurate prediction of damage and failure in laminated composites is still a major issue many structural applications. paper provides detailed description new mesomodel and...
archives-ouvertes.fr
harvard.edu
sagepub.com
sci-hub.se 参考文章(27)
P. Ladevèze, G. Lubineau, On a damage mesomodel for laminates: micro–meso relationships, possibilities and limits Composites Science and Technology. ,vol. 61, pp. 2149- 2158 ,(2001) , 10.1016/S0266-3538(01)00109-9
M J Hinton, A S Kaddour, P D Soden, Failure Criteria in Fibre-Reinforced-Polymer Composites: The World-Wide Failure Exercise ,(2004)
FW Crossman, ASD Wang, The Dependence of Transverse Cracking and Delamination on Ply Thickness in Graphite/Epoxy Laminates ASTM special technical publications. pp. 118- 139 ,(1982) , 10.1520/STP34324S
C Henaff-Gardin, M-C Lafarie-Frenot, J Brillaud, A El Mahi, Influence of the Stacking Sequence on Fatigue Transverse Ply Cracking in Cross-Ply Laminates ASTM International. ,(1992) , 10.1520/STP14577S
Michael R. Wisnom, Stephen R. Hallett, The role of delamination in strength, failure mechanism and hole size effect in open hole tensile tests on quasi-isotropic laminates Composites Part A-applied Science and Manufacturing. ,vol. 40, pp. 335- 342 ,(2009) , 10.1016/J.COMPOSITESA.2008.12.013
P LADEVEZE, E LEDANTEC, Damage modelling of the elementary ply for laminated composites Composites Science and Technology. ,vol. 43, pp. 257- 267 ,(1992) , 10.1016/0266-3538(92)90097-M
N.J. Pagano, G.A. Schoeppner, R. Kim, F.L. Abrams, Steady-state cracking and edge effects in thermo-mechanical transverse cracking of cross-ply laminates Composites Science and Technology. ,vol. 58, pp. 1811- 1825 ,(1998) , 10.1016/S0266-3538(98)00047-5
Pierre Ladevèze, Olivier Allix, Jean-François Deü, David Lévêque, A mesomodel for localisation and damage computation in laminates Computer Methods in Applied Mechanics and Engineering. ,vol. 183, pp. 105- 122 ,(2000) , 10.1016/S0045-7825(99)00214-5
O. Allix, P. Ladevèze, Interlaminar interface modelling for the prediction of delamination Composite Structures. ,vol. 22, pp. 235- 242 ,(1992) , 10.1016/0263-8223(92)90060-P
AS Kaddour, MJ Hinton, Maturity of 3D failure criteria for fibre-reinforced composites: Comparison between theories and experiments: Part B of WWFE-II: Journal of Composite Materials. ,vol. 47, pp. 925- 966 ,(2013) , 10.1177/0021998313478710